高强度钢和低温钢用焊条

Avesta 347-16焊条阿维斯塔进口不锈钢焊条

瑞典阿维斯塔焊条Avesta 309L-16焊条E309L-16不锈钢焊条

陕西西安骏焊专业阿维斯塔不锈钢焊条焊丝 镍基焊条焊丝等特种进口焊条焊丝

品名

类别

AWS型号

元素化学成份百分比

C

Si

Mn

Cr

Ni

Mo

骏焊瑞典阿维斯塔不锈钢

焊条

308L/MVR

E308L-17

0.02

0.8

1.0

20.0

10.5


308L/MVR

E308L-15

0.03

0.2

1.7

20.0

10.0


308L/MVR

E308L-16

0.03

0.3

1.5

20.0

10.0


308/308H

E308H-17

0.06

0.7

1.1

20.0

10.0


347/MVNb

E347-17

0.02

0.8

0.8

19.5

10.0


347/MVNb

E347-15

0.06

0.2

1.7

19.5

10.0


316L/SKR

E316L-17

0.02

0.8

1.1

18.5

12.0

2.8

316L/SKR

E316L-15

0.03

0.2

1.7

18.5

12.0

2.8

316L/SKR

E316L-16

0.02

0.3

1.4

19.0

12.0

2.8

316/316H

E316H-17

0.06

0.8

1.0

19.0

12.0

2.8

318/SKNb

E318-17

0.02

0.8

0.8

18.5

12.0

2.8

318/SKNb

E318-15

0.04

0.2

2.1

18.5

12.5

2.7

317L/SNR

E317L-17

0.02

0.7

0.9

19.0

13.0

3.7

2205

E2209-17

0.02

0.8

0.7

23.0

9.5

3.0

2205

E2209-15

0.02

0.5

0.8

23.0

9.5

3.0

904L

E385-17

0.02

0.8

1.2

20.5

25.0

4.5

383

E383-17

0.02

0.9

0.9

27.0

32.0

3.7

P12-R

EniCrMo-12

0.02

0.4

0.4

21.5


9.5

P625

EniCrMo-3

0.02

0.5

0.2

21.5


9.5

307

E307-17

0.07

0.8

4.0

20.0

10.5

0.8

309L

E309L-15

0.03

0.2

1.9

24.0

13.0


P5

E309MoL-17

0.02

0.8

1.1

22.5

13.5

2.7

P5

E309MoL-15

0.03

0.2

2.0

22.5

13.0

2.7

P5

E309MoL-16

0.03

0.3

1.4

22.5

13.5

2.7

P7

E312-17

0.09

0.8

0.8

29.0

9.5


P10

ENiCrFe-3

0.02

0.4

6.5

16.0



309

E309-17

0.05

0.8

1.0

24.0

13.5


310

E310-17

0.10

0.5

2.1

26.0

21.0


310

E310-15

0.12

0.3

2.4

25.5

21.


瑞典阿维斯塔347-16焊条.png

LB-52NSU日本神钢焊条 低合金低温钢高强钢焊条进口焊条进口焊丝

西安骏焊专业销售日本神钢焊条焊丝

4.1. trustarc LB-52NSU

When pipe root pass welding must be conducted from outside rather than inside in order to form the back bead inside the pipe, GTAW or SMAW are generally favored. Kobe Steel has long marketed FAMILIARC™ LB-52U as well as FAMILIARC™ LB-62U for this purpose, and they still serve as Kobe’s most reliable, “one and only” products worldwide.

In addition to meeting the always-changing and diverse specifications of pipelines, TRUSTARC™ LB-52NSU has been developed specifically for root pass welding of pipes for low temperature service. It is a covered, low hydrogen type electrode equivalent to AWS A5.5 E7016-G. It offers superb notch toughness at -60°C and very low diffusible hydrogen content of about 3.0ml/100g. The chemistries, mechanical properties of all weld metal and diffusible hydrogen content of TRUSTARC™ LB-52NSU are shown in Tables 3, 4 and 5 respectively.

Table 1: Covered electrodes for girth welding
API 5L
pipe
grade
Welding
pass
Low hydrogen typeHigh
cellulose
type
Vertical
upward
Vertical
downward
X42-X52RootLB-52U
LB-52NSU
LB-78VSKOBE-6010
HotLB-52-18
LB-52NS
Filler & Cap
X56-X60RootLB-52U
LB-52NSU
KOBE-6010
KOBE-7010S
HotLB-52-18
LB-52NS
KOBE-7010S
Filler & Cap
X65RootLB-52ULB-88VSKOBE-7010S
KOBE-8010S
HotLB-62
LB-62D
Filler & CapKOBE-8010S
X70RootLB-62UKOBE-7010S
KOBE-8010S
HotLB-62
LB-62D
Filler & CapKOBE-8010S
X80RootLB-62ULB-98VS
LB-108VS
——
HotLB-65D
LB-106
Filler & Cap
X100Root——LB-118VS——
HotLB-80L
LB-116
Filler & Cap
Table 2: TIG and MAG wires for girth welding
API 5L
pipe
grade
Welding
pass
Temperature (°C)
-20-40-60
X42-X56Root & HotTG-S50
MX-100T
TG-S1N
MX-A55T
Filler & CapDW-A50
DW-A50SR
DW-A55E
DW-A55ESR
DW-A55L
DW-A55LSR
DW-A81Ni1
X60Root & HotTG-S62TG-S60A
Filler & CapDW-A55E
DW-A55ESR
DW-A55L
DW-A55LSR
DW-A81Ni1
X65Root & HotTG-S62TG-S60A
Filler & CapDW-A55E
DW-A55ESR
DW-A55L
DW-A55LSR
DW-A81Ni1
X70Root & HotTG-S62TG-S60A
Filler & CapDW-A70LDW-A55L
DW-A81Ni1
X80Root & HotTG-S80AM
Filler & CapDW-A70L——
X100Root & HotTG-S80AM
Filler & CapDW-A80L————

Table 3: Chemistries of TRUSTARCTM LB-52NSU all weld metal (mass %)
CSiMnPSNiTiB
0.060.621.250.0160.0040.500.0140.0027
Table 4: Mechanical properties of TRUSTARCTM LB-52NSU all weld metal
Tensile propertiesNotch toughness
0.2%
PS
(MPa)
TS
(MPa)
EI
(%)
RA
(%)
Absorbed energy:J
(Brittle fracture: %)
FATT
(°C)
-80°C-60°C-40°C
511598327843(60)
55(60)
41(60)
Av.46(60)
44(55)
72(55)
58(52)
Av.58(54)
70(50)
137(35)
144(35)
Av.117(40)
-53
Table 5: Diffusible hydrogen content of TRUSTARCTM LB-52NSU (ml/100g)
Electrode dia (mm)1234Ave.
3.22.83.33.53.03.2

Note: Tested method: According to AWS A4.3.(Gas chromatography)
            Welding current: 120 A (DCEP)
            Welding atmosphere: 21°C x RH10%


Figure 3: Groove shape and pass sequence of butt joint welding with TRUSTARCTM LB-52NSU(root pass only) and TRUSTARCTM LB-52NS

Figure 3: Groove shape and pass sequence of butt joint
welding with TRUSTARCTM LB-52NSU(root pass only)
and TRUSTARCTM LB-52NS

In welding a butt joint on a 25 mm thick plate, 3.2 mm dia. TRUSTARC™ LB-52NSU was used for the root pass with DC 95 amp, and 3.2 mm dia. TRUSTARC™ LB-52NS was used for the second pass onwards with DC 110 amp in the vertical upward . The preheating and interpass temperatures were kept between 115 and 135°C. Figure 3 shows the groove shape and the pass sequence and Figure 4, the macrostructure of the weld metal. The chemistries and the tensile properties are shown in Tables 6 and 7, respectively and the notch toughness properties and the transition curve of the butt joint weld metal are shown in Table 8 and Figure 5, respectively. (Note: both TRUSTARC™ LB-52NSU and TRUSTARC™ LB-52NS are specified as AWS A5.5 E7016-G).

Figure 4: Macrostructure of butt joint weld me<em></em>tal

Figure 4: Macrostructure of butt joint weld 
metal

Table 6: Chemistries of butt joint weld metal (mass %)
LocationCSiMnPSNiTiB
Face0.070.311.400.0080.0030.500.0130.0022
Reverse0.080.301.360.0090.0030.430.0140.0023
Table 7: Tensile properties of butt joint weld metal
LocationTensile properties
Center0.2%PS
(MPa)
TS
(MPa)
El
(%)
RA
(%)
5065772581

公司联系方式 西安骏焊焊材有限公司 郑经理(经理)
  • 电话:029-86691076
  • 地址:雁塔区太白南路东侧新一代国际公寓1幢1单元
  • 手机:13891857851
  • 邮箱:1661780919@qq.com
  • QQ:1661780919
 
打赏
 
0相关评论

推荐图文
推荐资讯
最新资讯
公司新闻